Quartz crystal blank and quartz crystal resonator unit

ABSTRACT

A rectangular quartz crystal blank having long sides substantially parallel to a Z′ axis of the quartz crystal blank, and short sides substantially parallel to an X axis of the quartz crystal blank. The quartz crystal blank includes a first center region, a second region and a third region that are adjacent to the first region along a long-side direction, and a fourth region and a fifth region that are adjacent to the first region along a short-side direction. A thickness of the second region and a thickness of the third region are smaller than a thickness of the first region, and/or a thickness of the fourth region and a thickness of the fifth region are smaller than the thickness of the first region, and 13.84≦W/T≦14.33, where W is a length of a short side and T is a thickness.

CROSS REFERENCE TO RELATED APPLICATIONS

The present application is a continuation of International application No. PCT/JP2016/067442, filed Jun. 10, 2016, which claims priority to Japanese Patent Application No. 2015-118891, filed Jun. 12, 2015, the entire contents of each of which are incorporated herein by reference.

FIELD OF THE INVENTION

The present invention relates to an AT-cut quartz crystal blank and a quartz crystal resonator unit.

BACKGROUND OF THE INVENTION

As reduction in size of a quartz crystal resonator unit has been demanded in recent years, it is necessary to reduce the size of a quartz crystal blank. However, when the size of a quartz crystal blank is reduced, the influence of a sub-vibration becomes pronounced or an influence of vibration leakage arises, and therefore series resistance tends to increase. Examples of existing inventions related to a quartz crystal blank and aimed at reduction of series resistance include a quartz crystal resonator plate described in Patent Document 1. End portions of the quartz crystal resonator plate are chamfered (beveled). Thus, vibration energy is confined under excitation electrodes, and appropriate series resistance can be achieved.

As described above, regarding a quartz crystal blank, various improvements have been made in order to achieve appropriate series resistance.

-   Patent Document 1: Japanese Unexamined Patent Application     Publication No. 2013-34176

SUMMARY OF THE INVENTION

An object of the present invention is to provide a quartz crystal blank and a quartz crystal resonator unit that can reduce a crystal impedance (CI) value.

A quartz crystal blank according to an aspect of the present invention is an AT-cut quartz crystal blank that is plate-shaped and is rectangular when seen in a direction normal to a main surface. Long sides of the main surface are substantially parallel to a Z′ axis of the quartz crystal blank. Short sides of the main surface are substantially parallel to an X axis of the quartz crystal blank. A frequency of a main vibration of the quartz crystal blank is in a range of 36.0 MHz to 40.0 MHz. The quartz crystal blank includes a first region including a center of the main surface when seen in the direction normal to the main surface, a second region and a third region that are adjacent to the first region on both sides in a long-side direction in which the long sides extend, and a fourth region and a fifth region that are adjacent to the first region on both sides in a short-side direction in which the short sides extend. A thickness of the first region is substantially uniform. A thickness of the second region and a thickness of the third region are smaller than the thickness of the first region, and/or a thickness of the fourth region and a thickness of the fifth region are smaller than the thickness of the first region. 13.84≦W/T≦14.33 is satisfied, where W is a length of the first region, the fourth region, and the fifth region in the short-side direction, and T is the thickness of the first region.

The present invention is also directed at a quartz crystal resonator unit including the quartz crystal blank.

With the present invention, the CI value can be reduced.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an external perspective view of a quartz crystal resonator unit 10.

FIG. 2 is an exploded perspective view of the quartz crystal resonator unit 10.

FIG. 3 is a sectional view taken along line A-A of FIG. 1.

FIG. 4 is a sectional view taken along line B-B of FIG. 2.

FIG. 5 is a sectional view taken along line C-C of FIG. 2.

FIG. 6 is a top view of a quartz crystal blank 17.

FIG. 7 is an enlarged view of a region A1.

FIG. 8 is a graph representing the relationship between the frequencies of a main vibration and sub-vibrations and W/T of a quartz crystal blank 17 in which the frequency of the main vibration is 36.0 MHz.

FIG. 9 is a graph representing the relationship between the frequencies of a main vibration and sub-vibrations and W/T of a quartz crystal blank 17 in which the frequency of the main vibration is 37.4 MHz.

FIG. 10 is a graph representing the relationship between the frequencies of a main vibration and sub-vibrations and W/T of a quartz crystal blank 17 in which the frequency of the main vibration is 40.0 MHz.

FIG. 11 is graph representing the result of an experiment performed on first to fifth samples.

FIG. 12 is graph representing the result of an experiment performed on sixth to ninth samples.

FIG. 13 is a sectional view of a quartz crystal resonator unit 10 a according to a modification.

FIG. 14 is a sectional view of a quartz crystal oscillator 300.

FIG. 15 is a sectional view of a quartz crystal blank 17 a according to another embodiment.

FIG. 16 is a sectional view of a quartz crystal blank 17 b according to another embodiment.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

(Structure of Quartz Crystal Resonator Unit)

Hereinafter, a quartz crystal resonator unit that includes a quartz crystal blank according to an embodiment of the present invention will be described with reference to the drawings. FIG. 1 is an external perspective view of a quartz crystal resonator unit 10. FIG. 2 is an exploded perspective view of the quartz crystal resonator unit 10. FIG. 3 is a sectional view taken along line A-A of FIG. 1.

Hereinafter, a direction normal to the main surface of the quartz crystal resonator unit 10 is defined as the vertical direction, a direction in which the long sides of the quartz crystal resonator unit 10 extend when seen from above is defined as the long-side direction, and a direction in which the short sides of the quartz crystal resonator unit 10 extend is defined as the short-side direction. Hereinafter, structures may be described with respect to the axial directions of AT cut of a quartz crystal blank 17.

As illustrated in FIGS. 1 to 3, the quartz crystal resonator unit 10 includes a substrate 12, a metal cap 14, a quartz crystal resonator 16, and a brazing alloy 50. The width of the short sides of the quartz crystal resonator unit 10 is 1.0 mm, and the length of the long sides of the quartz crystal resonator unit 10 is 1.2 mm.

The substrate 12 (an example of a circuit substrate) includes a substrate body 21; outer electrodes 22, 26, 40, 42, 44, and 46; wiring lines 24, 27, and 49; via-hole conductors 25, 28, 54, and 56; and a metalized film 30.

The substrate body 21 is plate-shaped and is rectangular when seen from above. The substrate body 21 is made from, for example, a ceramic insulating material, such as an aluminum oxide sintered compact, a mullite sintered compact, an aluminum nitride sintered compact, a silicon carbide sintered compact, or a glass ceramic sintered compact; quartz crystal; glass; silicon; or the like. In the present embodiment, the substrate body 21 is a stack of insulating layers made of a ceramic material. The substrate body 21 has an upper main surface and a lower main surface. The upper main surface (main surface on the +Y′ side) of the substrate body 21 will be referred to as the “front surface”, and the lower main surface (main surface on the −Y′ side) of the substrate body 21 will be referred to as the “back surface”.

The outer electrodes 22 and 26 are disposed on an end portion of the front surface of the substrate body 21 in the long-side direction so as to be arranged in the short-side direction. To be specific, the outer electrode 22 is a rectangular conductor layer that is disposed near the corner on the −Z′ and +X side of the front surface of the substrate body 21. The outer electrode 26 is a rectangular conductor layer that is disposed near the corner on the −Z′ and −X side of the front surface of the substrate body 21.

The outer electrodes 40, 42, 44, and 46 are disposed near the respective corners of the back surface of the substrate body 21. The outer electrode 40 is a square conductor layer that is disposed near the corner on the −Z′ and −X side of the back surface of the substrate body 21. The outer electrode 40 overlaps the outer electrode 26 when seen from above. The outer electrode 42 is a square conductor layer that is disposed near the corner on the −Z′ and +X side of the back surface of the substrate body 21. The outer electrode 42 overlaps the outer electrode 22 when seen from above. The outer electrode 44 is a square conductor layer that is disposed near the corner on the +Z′ and −X side of the back surface of the substrate body 21. The outer electrode 46 is a square conductor layer that is disposed near the corner on the +Z′ and +X side of the back surface of the substrate body 21.

The via-hole conductor 25 extends through the substrate body 21 in the vertical direction and connects the outer electrode 22 and the outer electrode 42 to each other. The via-hole conductor 28 extends through the substrate body 21 in the vertical direction and connects the outer electrode 26 and the outer electrode 40 to each other.

The metalized film 30 is a linear metal film disposed on the front surface of the substrate body 21. The metalized film 30 is rectangular-ring shaped when seen from above (in the direction normal to the front surface). The outer electrodes 22 and 26 are disposed in a region surrounded by the metalized film 30 when seen from above.

The via-hole conductor 54 extends through the substrate body 21 in the vertical direction and connects the metalized film 30 and the outer electrode 46 to each other. The via-hole conductor 56 extends through the substrate body 21 in the vertical direction and connects the metalized film 30 and the outer electrode 44 to each other.

The outer electrodes 22, 26, 40, 42, 44, and 46 and the metalized film 30 have a three-layer structure. To be specific, the three-layer structure is formed by stacking a molybdenum layer, a nickel layer, and a gold layer from below. The via-hole conductors 25, 28, 54, and 56 are formed by embedding conductors, such as molybdenum, into via-holes formed in the substrate body 21.

The quartz crystal resonator 16 includes the quartz crystal blank 17, outer electrodes 97 and 98, excitation electrodes 100 and 101, and extension electrodes 102 and 103. The quartz crystal blank 17 is plate-shaped and is rectangular when seen from above. The upper main surface of the quartz crystal blank 17 will be referred to as the “front surface”, and the lower main surface of the quartz crystal blank 17 will be referred to as the “back surface”.

The quartz crystal blank 17 is an AT-cut quartz crystal blank that is cut from, for example, a rough quartz crystal at a predetermined angle. The long sides of the front surface and the back surface of the quartz crystal blank 17 are substantially parallel to the Z′ axis of the quartz crystal blank 17. The short sides of the front surface and the back surface of the quartz crystal blank 17 are substantially parallel to the X axis of the quartz crystal blank 17. Here, “substantially parallel” allows deviation within about ±1 degree relative to the Z′ axis and the X axis. The quartz crystal blank 17 is beveled, as described below in detail. In each of FIGS. 2 and 3, beveled portions are not illustrated.

The quartz crystal resonator unit is sized so that the length in the long-side direction is 1.2 mm and the width in the short-side direction is 1.0 mm. To achieve this size, in consideration of the thickness of a package wall, bleeding of a molding compound, and the precision of mounting an element, the quartz crystal blank 17 is designed so as have a length of 0.80 mm or smaller in the long-side direction and a width of 0.67 mm or smaller in the short-side direction.

The outer electrode 97 is a conductor layer that is disposed in a region including the corner on the −Z′ and +X side of the quartz crystal blank 17. The outer electrode 97 is formed on the front surface and the back surface of the quartz crystal blank 17 and also on side surfaces on the +X side and the −Z′ side of the quartz crystal blank 17. The outer electrode 98 is a conductor layer that is disposed in a region including the corner on the −Z′ and −X side of the quartz crystal blank 17. The outer electrode 98 is formed on the front surface and the back surface of the quartz crystal blank 17 and also on side surfaces on the −X side and the −Z′ side of the quartz crystal blank 17. Thus, the outer electrodes 97 and 98 are arranged along a short side of the quartz crystal blank 17.

The excitation electrode 100 is disposed at the center of the front surface of the quartz crystal blank 17 and is rectangular when seen from above. The excitation electrode 101 is disposed at the center of the back surface of the quartz crystal blank 17 and is rectangular when seen from above. The excitation electrode 100 and the excitation electrode 101 completely overlap each other when seen from above.

The extension electrode 102 is disposed on the front surface of the quartz crystal blank 17 and connects the outer electrode 97 and the excitation electrode 100 to each other. The extension electrode 103 is disposed on the back surface of the quartz crystal blank 17 and connects the outer electrode 98 and the excitation electrode 101 to each other. The outer electrodes 97 and 98, the excitation electrodes 100 and 101, and the extension electrodes 102 and 103 are each formed, for example, by stacking a gold layer on a chrome underlying layer.

The quartz crystal resonator 16 is mounted on the front surface of the substrate 12. To be specific, the outer electrode 22 and the outer electrode 97 are fixed to each other so as to be electrically connected to each other by using an electroconductive adhesive 210, and the outer electrode 26 and the outer electrode 98 are fixed to each other so as to be electrically connected to each other by using an electroconductive adhesive 212.

The metal cap 14 is a housing that has a rectangular opening. The metal cap 14 is made, for example, by plating a base metal, such as an iron-nickel alloy or a cobalt-nickel alloy, with nickel and gold. In the present embodiment, the metal cap 14 is a rectangular-parallelepiped box whose lower side is open. The metal cap 14 is made by plating a base metal, which is an iron-nickel alloy, with nickel and gold.

The brazing alloy 50 is disposed on the metalized film 30. The brazing alloy 50 has substantially the same shape as the metalized film 30 and is rectangular-ring shaped. The brazing alloy 50 has a melting point lower than that of the metalized film 30 and is made of, for example, a gold-tin alloy. The brazing alloy 50 is formed on the metalized film 30 by, for example, printing or the like. The metalized film 30 is melted and solidified in a state in which the outer edge of the opening of the metal cap 14 is in contact with the brazing alloy 50. Thus, the metal cap 14 is joined to the metalized film 30 via the brazing alloy 50 along the entire length of the outer edge of the opening. As a result, the front surface of the substrate body 21 and the metal cap 14 form a hermetically sealed space Sp. Accordingly, the quartz crystal resonator 16 is contained in the hermetically sealed space Sp. Since the metal cap 14 is in close contact with the substrate body 21 via the metalized film 30 and the brazing alloy 50, the inside of the hermetically sealed space Sp is maintained in a vacuum state. However, the inside may be in an atmospheric state. Instead of the brazing alloy 50, for example, an adhesive made of low-melting-point glass, a resin, or the like may be used. In this case, the metalized film 30 may be omitted.

(Details of Quartz Crystal Blank)

Hereinafter, details of the quartz crystal blank 17 will be described with reference to the drawings. FIG. 4 is a sectional view taken along line B-B of FIG. 2. FIG. 5 is a sectional view taken along line C-C of FIG. 2. FIG. 6 is a top view of the quartz crystal blank 17. FIG. 7 is an enlarged view of a region A1.

In order to reduce the CI value, the quartz crystal blank 17 according to the present embodiment satisfies the following conditions.

Condition 1: The frequency of a main vibration of the quartz crystal blank 17 is in the range of 36.0 MHz to 40.0 MHz.

Condition 2: The long sides of the front surface and the back surface of the quartz crystal blank 17 are substantially parallel to the Z′ axis of the quartz crystal blank 17.

Condition 3: The short sides of the front surface and the back surface of the quartz crystal blank 17 are substantially parallel to the X axis of the quartz crystal blank 17.

Condition 4: The quartz crystal blank 17 is beveled so that, as illustrated in FIGS. 4 and 5, the thickness of portions of the quartz crystal blank 17 near the outer edges of the front surface and the back surface of the quartz crystal blank 17 is smaller than the thickness of a portion of the quartz crystal blank 17 near the centers of the front surface and the back surface of the quartz crystal blank 17.

Condition 5: 13.84≦W/T≦14.33 is satisfied, where W is the length of regions A1, A4, and A5 of the quartz crystal blank 17 in the short-side direction, and T is the thickness of the region A1 of the quartz crystal blank 17. The regions A1, A4, and A5 will be described below.

<Regarding Condition 1>

The frequency of the main vibration of the quartz crystal blank 17 depends on the thickness T of the quartz crystal blank 17. Accordingly, the thickness T of the quartz crystal blank 17 is set in the range of 0.0418 mm to 0.0464 mm.

<Regarding Conditions 2 and 3>

In general, a quartz crystal blank is fixed to a substrate by bonding a portion of the quartz crystal blank near a short side thereof to the substrate by using an electroconductive adhesive. Moreover, it is known that the vibration direction of a thickness shear vibration of an AT-cut quartz crystal blank is the X-axis direction. Accordingly, an existing quartz crystal blank whose long sides are parallel to the X axis is likely to influence the substrate due to vibration leakage via the electroconductive adhesive near the short side. In contrast, in the AT-cut quartz crystal blank 17 according to the present embodiment, vibration leakage to a Z′ axis region is small, because the long sides are parallel to the Z′ axis. Therefore, even when the quartz crystal blank 17 is fixed to the substrate 12 by bonding a portion of the quartz crystal blank 17 near a short side thereof by using the electroconductive adhesives 210 and 212, the influence of vibration leakage on the substrate 12 is small. Accordingly, with the AT-cut quartz crystal blank according to the present embodiment, the influence of vibration leakage is smaller and the CI value is better than a quartz crystal blank whose long sides are parallel to the X axis.

<Regarding Condition 4>

As illustrated in FIG. 6, the quartz crystal blank 17 includes regions A1 to A5 when seen from above. The region A1 is a rectangular region including the center of the front surface when seen from above. The region A2 is a rectangular region adjacent to the region A1 on the +Z′ side. However, the shape of the region A1 may be non-rectangular when seen from above and may be, for example, elliptical. The region A2 is in contact with the entirety of a short side of the front surface on the +Z′ side and with end portions, in the +Z′ direction, of long sides of the front surface on the −X side and +X side. That is, the region A2 is positioned at an end portion of the quartz crystal blank 17 in the +Z′ direction. The region A3 is a rectangular region adjacent to the region A1 on the −Z′ side. The region A3 is in contact with the entirety of a short side of the front surface on the −Z′ side and with end portions, in the −Z′ direction, of the long sides of the front surface on the −X side and +X side. That is, the region A3 is positioned at an end portion of the quartz crystal blank 17 in the −Z′ direction.

The region A4 is a rectangular region that is adjacent to the region A1 on the −X side and interposed between the regions A2 and A3 from the left and right sides. The region A4 is in contact with a portion, excluding both ends, of a long side of the front surface on the −X side. That is, the region A4 is positioned at an end portion of the quartz crystal blank 17 in the −X direction. The region A5 is a rectangular region that is adjacent to the region A1 on the +X side and interposed between the regions A2 and A3 from the right and left sides. The region A5 is in contact with a portion, excluding both ends, of a long side of the front surface on the +X side. That is, the region A5 is positioned at an end portion of the quartz crystal blank 17 in the +X direction.

As illustrated in FIGS. 4 and 5, the thickness T of the region A1 is substantially uniform. However, the front surface and back surface of the region A1 are slightly curved. Accordingly, as illustrated in FIG. 7, the region A1 that is substantially uniform is a region having a thickness in the range of (Tmax−2 μm) to Tmax, where Tmax is the maximum value of the thickness of the quartz crystal blank in the region A1. The region A1 is a region that includes the center of the front surface and that is continuous. The thickness T of the region A1, which is substantially uniform, has the value Tmax.

As illustrated in FIGS. 4 and 5, the thicknesses of the regions A2 to A5 are smaller than the thickness T of the region A1. In the present embodiment, the thicknesses of the regions A2 to A5 continuously decrease with increasing distance from the region A1. In the present embodiment, the front surfaces and the back surfaces of the regions A2 to A5 are convex surfaces.

<Regarding Condition 5>

13.84≦W/T≦14.33 is satisfied, where W is the length of the regions A1, A4, and A5 of the quartz crystal blank 17 in the short-side direction, and T is the thickness of the region A1 of the quartz crystal blank 17. Preferably, 13.97≦W/T≦14.24 is satisfied.

<Regarding Other Conditions>

Preferably, in addition to the conditions 1 to 5, 0.60≦RL/L≦0.95 is satisfied, where L is the length of the regions A1 to A3 in the long-side direction, and RL is the length of the region A1 in the long-side direction; and 0.56≦RW/W≦0.95 is satisfied, where RW is the length of the region A1 in the short-side direction. More preferably, 0.60≦RL/L≦0.70 is satisfied, where L is the length of the regions A1 to A3 in the long-side direction, and RL is the length of the region A1 in the long-side direction; and 0.56≦RW/W≦0.64 is satisfied, where RW is the length of the region A1 in the short-side direction. Here, the length RL is the length of a portion of the region A1 extending in the long-side direction and passing through a point in the region A1 where the thickness is Tmax. The length RW is the length of a portion of the region A1 extending in the short-side direction and passing through the point in the region A1 where the thickness is Tmax.

(Method of Manufacturing Quartz Crystal Resonator Unit)

Hereinafter, a method of manufacturing the quartz crystal resonator unit 10 will be described with reference to the drawings.

First, a method of manufacturing the substrate 12 will be described. A mother substrate in which a plurality of substrate bodies 21 are arranged in a matrix pattern is prepared. The mother substrate is made from, for example, a ceramic insulating material, such as an aluminum oxide sintered compact, a mullite sintered compact, an aluminum nitride sintered compact, a silicon carbide sintered compact, or a glass ceramic sintered compact; quartz crystal; glass; silicon; or the like.

Next, through-holes are formed by irradiating, with a beam, positions on the mother substrate at which the via-hole conductors 25, 28, 54, and 56 of the substrate body 21 are to be formed. Moreover, the through-holes are filled with an electroconductive material, such as molybdenum, and the electroconductive material is dried. Subsequently, the via-hole conductors 25, 28, 54, and 56 are formed by firing the electroconductive material.

Next, underlying electrodes of the outer electrodes 40, 42, 44, and 46 are formed on the back surface of the mother substrate. To be specific, a molybdenum layer is printed on the back surface of the mother substrate and dried. Subsequently, the molybdenum layer is fired. Thus, the underlying electrodes of the outer electrodes 40, 42, 44, and 46 are formed.

Next, underlying electrodes of the outer electrodes 22 and 26 and the metalized film 30 are formed on the front surface of the mother substrate. A molybdenum layer is printed on the front surface of the mother substrate and dried. Subsequently, the molybdenum layer is fired. Thus, the underlying electrodes of the outer electrodes 22 and 26 and the metalized film 30 are formed.

Next, the underlying electrodes of the outer electrodes 40, 42, 44, 46, 22, and 26 and the metalized film 30 are plated with nickel and gold in this order. Thus, the outer electrodes 40, 42, 44, 46, 22, and 26 and the metalized film 30 are formed.

Here, by using a vacuum printing method or the like, it is possible to simultaneously perform filling of the through-holes with the electroconductive material and printing of the outer electrode and the like on the mother substrate. At this time, the electroconductive material, the outer electrodes, and the like are simultaneously fired.

When the mother substrate is made from a ceramic sintered compact insulating material, while the mother substrate is in a sheet shape before being fired, through-holes are formed, the through-holes are filled with the electroconductive material, and the outer electrodes 22, 26, 40, 42, 44, and 46 and the metalized film 30 are printed and dried. Subsequently, a plurality of such sheets are stacked and press-bonded to form a stacked sheet. By firing the stacked sheet, it is possible to simultaneously form the via-hole conductors; the outer electrodes 22, 26, 40, 42, 44, and 46; the metalized film 30; and the substrate body 21. Subsequently, plating is performed in the same way as described above.

Next, the mother substrate is divided into a plurality of substrate bodies 21 by using a dicer.

Next, a method of manufacturing the quartz crystal resonator 16 will be described. The quartz crystal blank 17, which is rectangular plate-shaped, is obtained by AT-cutting a rough quartz crystal. At this time, the rough quartz crystal is cut so that the long sides of the front surface and the back surface of the quartz crystal blank 17 are substantially parallel to the Z′ axis of the quartz crystal blank 17 and the short sides of the front surface and the back surface of the quartz crystal blank 17 are substantially parallel to the X axis of the quartz crystal blank 17.

Next, the quartz crystal blank 17 is beveled by using a barrel finishing apparatus. Thus, ridge portions of the quartz crystal blank 17 are ground, and, as illustrated in FIGS. 4 and 5, the quartz crystal blank 17 has a cross-sectional shape such that the thickness thereof decreases with increasing distance from the center of the front surface.

Next, the outer electrodes 97 and 98, the excitation electrodes 100 and 101, and the extension electrodes 102 and 103 are formed on the quartz crystal blank 17. Since the outer electrodes 97 and 98, the excitation electrodes 100 and 101, and the extension electrodes 102 and 103 can be formed through a general process, the description of the process will be omitted.

Next, the quartz crystal resonator 16 is mounted on the front surface of the substrate body 21. To be specific, as illustrated in FIGS. 2 and 3, the outer electrode 22 and the outer electrode 97 are bonded to each other by using the electroconductive adhesive 210, and the outer electrode 26 and the outer electrode 98 are bonded to each other by using the electroconductive adhesive 212.

Next, the metal cap 14 is attached to the substrate 12 by using the brazing alloy 50. Through the process described above, the quartz crystal resonator unit 10 is completed.

Advantageous Effects

With the quartz crystal blank 17 and the quartz crystal resonator unit 10 according to the present embodiment, the CI value can be reduced. To be more specific, as illustrated in FIGS. 4 and 5, the quartz crystal blank 17 has a sectional shape such that the thickness thereof decreases with increasing distance from the center of the front surface. Thus, the vibration energy of the main vibration of the quartz crystal blank 17 is confined in the region A1. The excitation electrodes 100 and 101 are disposed on the region A1. As a result, the main vibration is efficiently converted into an electric signal, and the electric signal is output from the excitation electrodes 100 and 101. Thus, with the quartz crystal blank 17 and the quartz crystal resonator unit 10, the CI value can be reduced.

With the quartz crystal blank 17 and the quartz crystal resonator unit 10, the CI value can be reduced also for the following reasons. FIG. 8 is a graph representing the relationship between the frequencies of a main vibration and sub-vibrations and W/T of a quartz crystal blank 17 in which the frequency of the main vibration is 36.0 MHz. FIG. 9 is a graph representing the relationship between the frequencies of a main vibration and sub-vibrations and W/T of a quartz crystal blank 17 in which the frequency of the main vibration is 37.4 MHz. FIG. 10 is a graph representing the relationship between the frequencies of a main vibration and sub-vibrations and W/T of a quartz crystal blank 17 in which the frequency of the main vibration is 40.0 MHz. In each of FIGS. 8 to 10, the triangles represent the main vibration, and the squares and the rhombuses represent the sub-vibrations.

In the quartz crystal blank 17 and the quartz crystal resonator unit 10, sub-vibrations occur in addition to a main vibration. The main vibration is a thickness shear vibration. The frequency of the main vibration depends on the thickness T of the quartz crystal blank 17. The sub-vibrations, which are vibrations other than the main vibration, occur due to extension and contraction of the quartz crystal blank 17 in the short-side direction, extension and contraction of the quartz crystal blank 17 in the long-side direction, warping of the quartz crystal blank 17, and the like. The frequencies of the sub-vibrations depend on the length L, the width W, and the like. Such sub-vibrations are so-called spurious vibrations. As can be understood from the results of simulation described below, in which W/T was changed while keeping the length L of the quartz crystal blank 17 in the long-side direction constant, sub-vibrations that may occur in the quartz crystal blank 17 and the quartz crystal resonator unit 10 can be suppressed by adjusting W/T.

Here, the CI value of the quartz crystal blank 17 and of the quartz crystal resonator unit 10 can be reduced by designing the quartz crystal blank 17 and the quartz crystal resonator 16 so as to separate the frequency of the main vibration from the frequencies of the sub-vibrations. The inventors studied the relationship between W/T and the frequencies of the main vibration and the sub-vibrations by performing computer simulation. In the computer simulation, for three types of quartz crystal blanks 17 having main vibration frequencies of 36.0 MHz, 37.4 MHz, and 40.0 MHz, the width W was changed while keeping the thickness T constant. The simulation conditions are as follows.

(1) 36.0 MHz

thickness T: 0.0464 mm

length L: 0.800 mm

length RL: 0.533 mm

RW/W: 0.64

(2) 37.4 MHz

thickness T: 0.0447 mm

length L: 0.800 mm

length RL: 0.533 mm

RW/W: 0.64

(3) 40.0 MHz

thickness T: 0.0418 mm

length L: 0.800 mm

length RL: 0.533 mm

RW/W: 0.64

By performing simulation under the above conditions, the results shown in FIGS. 8 to 10 were obtained. Then, the inventors investigated preferable W/T on the basis of the simulation results.

As can be seen from FIG. 8, when the frequency of the main vibration is 36.0 MHz, the main vibration and sub-vibrations 1 and 2 do not intersect if W/T is in the range of 13.84 to 14.33. That is, if W/T is in the range of 13.84 to 14.33 (that is, T is 0.0464 mm and W is in the range of 0.642 mm to 0.665 mm), the frequency of the main vibration is separated from the frequencies of the sub-vibrations.

As can be seen from FIG. 9, when the frequency of the main vibration is 37.4 MHz, the main vibration and the sub-vibrations 1 and 2 do not intersect if W/T is in the range of 13.84 to 14.33. That is, if W/T is in the range of 13.84 to 14.33 (that is, T is 0.0447 mm and W is in the range of 0.618 mm to 0.640 mm), the frequency of the main vibration is separated from the frequencies of the sub-vibrations.

As can be seen from FIG. 10, when the frequency of the main vibration is 40.0 MHz, the main vibration and the sub-vibrations 1 and 2 do not intersect if W/T is in the range of 13.84 to 14.34. That is, if W/T is in the range of 13.84 to 14.34 (that is, T is 0.0418 mm and W is in the range of 0.578 mm to 0.599 mm), the frequency of the main vibration is separated from the frequencies of the sub-vibrations.

These results show that, when the frequency of the main vibration of the quartz crystal blank 17 is in the range of 36.0 MHz to 40.0 MHz, the frequency of the main vibration is separated from the frequencies of the sub-vibrations if 13.84≦W/T≦14.33. Thus, in the quartz crystal blank 17 in which the frequency of the main vibration is in the range of 36.0 MHz to 40.0 MHz, the CI value can be reduced if 13.84≦W/T≦14.33.

Since a main vibration and sub-vibrations can be individually analyzed by using simulation, simulation has an advantage in that a range in which the influence of sub-vibrations on a main vibration in the range of 36.0 MHz to 40.0 MHz can be obtained by using the CI value. However, by measuring the CI values of actual samples, although only the CI value in which a main vibration and sub-vibrations are superposed can be obtained, it is possible to obtain detailed measurement results that reflect actual variations in dimensions, shapes, material characteristics, and the like. Therefore, the inventors performed an experiment using samples that were actually made as described below, and obtained a more preferable range of W/T in the frequency range of 36.0 MHz to 40.0 MHz. To be more specific, the inventors made forty pieces of each of first to fifth samples of the quartz crystal resonator unit 10. The conditions for the first to fifth samples are as follows.

First to fifth samples (frequency of main vibration: 37.4 MHz)

TABLE 1 First Second Third Fourth Fifth Sample Sample Sample Sample Sample T [mm] 0.0447 0.0447 0.0447 0.0447 0.0447 L [mm] 0.800 0.800 0.800 0.800 0.800 RL [mm] 0.543 0.527 0.522 0.531 0.518 W [mm] 0.624 0.627 0.630 0.633 0.636 RW [mm] 0.400 0.382 0.382 0.382 0.374

For each of the first to fifth samples, the CI value was measured. In the experiment, the ambient temperature was changed from −30° C. to 85° C. As the CI value, the maximum value for each sample when the temperature was changed from −30° C. to 85° C. was used.

FIG. 11 is a graph representing the result of the experiment performed on the first to fifth samples (the frequency of the main vibration: 37.4 MHz). In FIG. 11, the vertical axis represents the CI value, and the horizontal axis represents the width W.

FIG. 11 shows measurements of the CI value for W in the range of 0.624 mm to 0.636 mm where the CI value was smaller than or equal to 80Ω, which is about twice a small average CI value of 37Ω for W of 0.630 mm, in the case where the frequency of the main vibration was 37.4 MHz. In the case where the thickness T, which is determined from the frequency of the main vibration, was 0.0447 mm, the CI value was smaller than or equal to 80Ω and sufficiently low when W/T was in the range of 13.97 to 14.24.

Next, the inventors performed an experiment as described below and obtained preferable ranges of RL/L and RW/W. To be more specific, forty pieces of each of sixth to ninth samples were made. Conditions for the sixth to ninth samples were as follows.

Sixth to ninth samples (frequency of main vibration: 37.4 MHz)

TABLE 2 Sixth Seventh Eighth Ninth Sample Sample Sample Sample T [mm] 0.0447 0.0447 0.0447 0.0447 L [mm] 0.800 0.800 0.800 0.800 RL [mm] 0.483 0.503 0.522 0.561 W [mm] 0.630 0.630 0.630 0.630 RW [mm] 0.355 0.375 0.382 0.403

For each of the sixth to ninth samples, the CI value was measured. In the experiment, the ambient temperature was changed from −30° C. to 85° C. As the CI value, the maximum value for each sample when the temperature was changed from −30° C. to 85° C. was used.

FIG. 12 is a graph representing the result of the experiment performed on the sixth to ninth samples (the frequency of the main vibration: 37.4 MHz). In FIG. 12, the vertical axis represents the CI value, and the horizontal axis represents RL/L and RW/W.

FIG. 12 shows measurements of the CI value for RW/W in the range of 0.56 to 0.64 and RL/L in the range of 0.60 to 0.70 where the CI value was smaller than or equal to 80Ω in the case where the frequency of the main vibration was 37.4 MHz.

However, from FIG. 12, it is considered that the CI value can in a range such that the quartz crystal resonator unit is sufficiently useable even if RW/W is greater than 0.64 and RL/L is greater than 0.70. Therefore, in the case where the frequency of the main vibration of the quartz crystal blank 17 is 37.4 MHz, if 0.60≦RL/L≦0.95 and 0.56≦RW/W≦0.95, the CI value is at a level such that the quartz crystal resonator unit can oscillate, even though the CI value is high. The upper limit of RL/L and RW/W is set at 0.95 because, if RL/L and RW/W are greater than 0.95, the vibration energy of the main vibration of the quartz crystal blank 17 cannot be sufficiently confined in the region A1.

(Modification)

Hereinafter, a quartz crystal resonator unit 10 a according to a modification will be described with reference to the drawings. FIG. 13 is a sectional view of the quartz crystal resonator unit 10 a according to the modification.

As illustrated in FIG. 13, the quartz crystal resonator unit 10 a according to the present modification includes a quartz crystal resonator 16 including a quartz crystal blank 17, and differs from the quartz crystal resonator unit 10 according to the embodiment described above in that a thermistor 60 is disposed on a back surface of a substrate 12. As the quartz crystal blank 17, a quartz crystal blank according to the embodiment described above can be used.

(Quartz Crystal Oscillator)

Hereinafter, a quartz crystal oscillator 300 including a quartz crystal blank 17 will be described with reference to the drawings. FIG. 14 is a sectional view of the quartz crystal oscillator 300.

As illustrated in FIG. 14, the quartz crystal oscillator 300 includes a quartz crystal resonator 16 including the quartz crystal blank 17, and differs from the quartz crystal resonator unit 10 shown in FIG. 3 in that an IC 302 is mounted on a back surface of a substrate 12. As the quartz crystal blank 17, a quartz crystal blank according to the embodiment described above can be used.

Other Embodiments

A quartz crystal blank and a quartz crystal resonator unit according to the present invention are not limited to the quartz crystal blank 17 and the quartz crystal resonator unit 10, and may be modified within the scope of the present invention.

The quartz crystal blank 17 has a shape such that the thickness thereof decreases with increasing distance from the center of the front surface in the short-side direction and in the long-side direction. However, the thickness of the quartz crystal blank 17 may decrease with increasing distance from the center of the front surface in the short-side direction or may decrease with increasing distance from the center of the front surface in the long-side direction. That is, it is sufficient that the thickness of the region A2 and the thickness of the region A3 are smaller than the thickness of the region A1 and/or the thickness of the region A4 and the thickness of the region A5 are smaller than the thickness of the region A1.

FIGS. 15 and 16 are sectional views of quartz crystal blanks 17 a and 17 b according to other embodiments. As illustrated in FIG. 15, a region having a larger thickness than the region A2 may be disposed on the +Z′ side of the region A2; and a region having a larger thickness than the region A3 may be disposed on the −Z′ side of the region A3. Likewise, a region having a larger thickness than the region A4 may be disposed on the −X side of the region A4. A region having a larger thickness than the region A5 may be disposed on the +X side of the region A5. That is, as long as the region A2 to A5, each of which has a smaller thickness than the region A1, are disposed around the region A1, vibration energy of a main vibration is confined in the region A1. Therefore, other regions may be present or may not be present around the regions A2 to A5.

The regions A2 to A5, which have continuously-changing convex surfaces, may have concave surfaces or discontinuously-changing surfaces. That is, as illustrated in FIG. 16, the regions A2 to A5 may have step-like shapes.

As described above, the present invention can be used for a quartz crystal blank and a quartz crystal resonator unit and, in particular, advantageous in that the CI value can be reduced.

REFERENCE SIGNS LIST

-   -   10, 10 a quartz crystal resonator unit     -   12 substrate     -   14 metal cap     -   16 quartz crystal resonator     -   17, 17 a, 17 b quartz crystal blank     -   21 substrate body     -   22, 26, 40, 42, 44, 46 outer electrode     -   30 metalized film     -   50 brazing alloy     -   60 thermistor     -   100, 101 excitation electrode     -   300 quartz crystal oscillator     -   A1 to A5 region 

1. An AT-cut quartz crystal blank comprising: a quartz crystal body that is rectangular in shape in a direction normal to a main surface thereof, the quartz crystal body having a first region including a center of the main surface in the direction normal to the main surface, a second region and a third region that are adjacent to the first region on opposed sides thereof along a long-side direction in which long sides of the quartz crystal body extend, and a fourth region and a fifth region that are adjacent to the first region on opposed sides thereof along a short-side direction in which short sides of the quartz crystal body extend, wherein the long sides of the main surface are substantially parallel to a Z′ axis of the quartz crystal blank, wherein the short sides of the main surface are substantially parallel to an X axis of the quartz crystal blank, wherein a frequency of a main vibration of the quartz crystal blank is in a range of 36.0 MHz to 40.0 MHz, wherein a thickness of the first region is substantially uniform, wherein at least one of (1) a thickness of the second region and a thickness of the third region are smaller than the thickness of the first region, and (2) a thickness of the fourth region and a thickness of the fifth region are smaller than the thickness of the first region, and wherein 13.84≦W/T≦14.33, where W is a length of the first region, the fourth region, and the fifth region along the short-side direction, and T is the thickness of the first region.
 2. The quartz crystal blank according to claim 1, wherein 13.97≦W/T≦14.24.
 3. The quartz crystal blank according to claim 1, wherein the thickness of the second region and the thickness of the third region are smaller than the thickness of the first region, and the thickness of the fourth region and the thickness of the fifth region are smaller than the thickness of the first region.
 4. The quartz crystal blank according to claim 1, wherein the thickness of the second region and the thickness of the third region are smaller than the thickness of the first region.
 5. The quartz crystal blank according to claim 1, wherein the thickness of the fourth region and the thickness of the fifth region are smaller than the thickness of the first region.
 6. The quartz crystal blank according to claim 3, wherein the second region and the third region are positioned at opposed ends of the quartz crystal blank in the long-side direction, and wherein the fourth region and the fifth region are positioned at opposed ends of the quartz crystal blank in the short-side direction.
 7. The quartz crystal blank according to claim 6, wherein a thickness of the quartz crystal blank decreases with increasing distance from the center of the main surface in the long-side direction and decreases with increasing distance from the center of the main surface in the short-side direction.
 8. The quartz crystal blank according to claim 6, wherein a thickness of the quartz crystal blank decreases with increasing distance from the center of the main surface in the long-side direction.
 9. The quartz crystal blank according to claim 6, wherein a thickness of the quartz crystal blank decreases with increasing distance from the center of the main surface in the short-side direction.
 10. The quartz crystal blank according to claim 6, wherein 0.60≦RL/L≦0.95, where L is a length of the first region, the second region, and the third region along the long-side direction, and RL is a length of the first region along the long-side direction, and wherein 0.56≦RW/W≦0.95, where RW is a length of the first region along the short-side direction.
 11. The quartz crystal blank according to claim 10, wherein 0.60≦RL/L≦0.70, and wherein 0.56≦RW/W≦0.64.
 12. A quartz crystal resonator unit comprising: the quartz crystal blank according to claim
 1. 13. The quartz crystal resonator unit according to claim 12, comprising: a first outer electrode and a second outer electrode that are each arranged along a respective short side of the quartz crystal blank; a substrate body; and a third outer electrode and a fourth outer electrode that are each disposed on a respective main surface of the substrate body, wherein the first outer electrode and the third outer electrode are electrically connected to each other, and the second outer electrode and the fourth outer electrode are electrically connected to each other.
 14. The quartz crystal resonator unit according to claim 13, further comprising: a cap disposed on the substrate body and covering the quartz crystal resonator. 